this post was submitted on 24 Nov 2024
8 points (100.0% liked)

3DPrinting

15644 readers
249 users here now

3DPrinting is a place where makers of all skill levels and walks of life can learn about and discuss 3D printing and development of 3D printed parts and devices.

The r/functionalprint community is now located at: !functionalprint@kbin.social or !functionalprint@fedia.io

There are CAD communities available at: !cad@lemmy.world or !freecad@lemmy.ml

Rules

If you need an easy way to host pictures, https://catbox.moe may be an option. Be ethical about what you post and donate if you are able or use this a lot. It is just an individual hosting content, not a company. The image embedding syntax for Lemmy is ![](URL)

Moderation policy: Light, mostly invisible

founded 1 year ago
MODERATORS
j4k3@lemmy.world
andypiper@lemmy.world
henry_rowengartner@lemmy.world
GrayBackgroundMusic@lemm.ee
8
Trouble with warping (feddit.dk)
submitted 10 hours ago* (last edited 10 hours ago) by Grippler@feddit.dk to c/3dprinting@lemmy.world
9 comments fedilink hide all child comments
 

I have some very consistent issues with warping when printing ASA/ABS, which is really annoying since I'm trying to print my voron parts. It's not warping massively, but enough to mess things up.

I print with these general settings, on a textured PEI flex-plate.

  • heated chamber @ 45-47C (can't go much higher)
  • bed temp @105C
  • first layer 255C, other layers 245C
  • fan off, unless it's an overhang >=50% or layer time is <10s. Fan maxes out @70% unless bridging.
  • speed 200/120 mm/s inner/outer walls
  • first layer 50mm/s, 80mm/s infill

I've tried both with my regular Z-offset which creates a good uniform first layer, and slightly lower to kind of push it more on to the plate (but worse looking)

  • I've cleaned the plate with pure IPA
  • I've tried glue stick
  • I've tried brim both skirts/mouse ears, which help but don't eliminate it. (5mm, 0.15mm space)

ABS seems to be a little easier to print than the ASA. I'm using filament from Polymaker

you are viewing a single comment's thread
view the rest of the comments
[–] IMALlama@lemmy.world 1 points 4 hours ago* (last edited 4 hours ago)

I've run 15 kg or so of filmmaker ASA through my Voron.

Things I've learned:

  1. Let your printer heat soak, especially if you're printing a bigger part. Heat helps your print. It will also give your printer frame time to stabilize. My Voron grows in z as it heats up. I've printed multiple objects sequentially in one print without letting it heat soak and watched the first layers get worse and worse as the nozzle wound up further and further from the bed on each successive object
  2. Clean your bed. IPA is all well and good, but dish soap, your fingers to clean, and paper towel to dry is better. If your PEI sheet is new, scuffing it up some isn't a bad idea. You can use the rough side of a new yellow sponge for this, but you'll want to make that sponge a cleaning sponge afterwards
  3. Some shapes are more warp prone than others. If you design your own parts you can design around this to a certain extent. Avoid sharp corners and big aspect ratios (eg much wider than deep, etc)
  4. A printing a draft shield around your part will probably help
  5. Get your chamber warmer. You can do this with a mix of bed fans and insulation. My biggest print to date was pulled off with a 60 degree chamber. It had zero warping. My printer couldn't hit that chamber temp stock

Other ideas:

  • I've never used adhesive promotors on my bed
  • Even with a part stuck to the bed, I've had it warp 4-5 inches above the bed and crack before I figured out how to get my chamber temp up
  • With a big enough print I've pulled my bed plate up from the magnet thanks to warping. Again, the only solution I found for this was getting my chamber temp up
  • I personally run my bed at 100 °C and haven't had any issues
  • I've found Polymaker's ASA very easy to print on the cooler side, so I like to run it at 240 first layer/230 subsequent layers. Maybe try a temp tower? I was using 245 initially and was getting tons of wispy (super fine) stringing
  • With a warmer chamber you can run more fan since you won't be cooling the part as much